Διμεταλλικά ανοδικά ηλεκτρόδια Pt-TiO2 για την ηλεκτροχημική οξείδωση αλκοολών σε κυψελίδες καυσίμου χαμηλών θερμοκρασιών
| dc.contributor.advisor | Γιαννούλης, Παναγιώτης | |
| dc.contributor.author | Hasa, Bjorn | |
| dc.contributor.committee | Κατσαούνης, Αλέξανδρος | |
| dc.contributor.committee | Βαγενάς, Κωνσταντίνος | |
| dc.contributor.committee | Γιαννούλης, Παναγιώτης | |
| dc.contributor.other | Χάσα, Μπιορν | |
| dc.date.accessioned | 2013-10-11T19:09:23Z | |
| dc.date.available | 2013-10-11T19:09:23Z | |
| dc.date.copyright | 2013-06-24 | |
| dc.date.issued | 2013-10-11 | |
| dc.degree | Μεταπτυχιακή Εργασία | el |
| dc.description.abstract | Σε αυτή την μελέτη διμεταλλικά ηλεκτρόδια Pt-TiO2 παρασκευάστηκαν και χαρακτηρίστηκαν με περίθλαση ακτίνων Χ (X-ray diffraction - XRD), με ηλεκτρονικό μικροσκόπιο σάρωσης (Scanning Electron Microscopy - SEM), φασματοσκοπία φωτοηλεκτρονίων από ακτίνες Χ (X-ray photoelectron spectroscopy - XPS), ηλεκτροχημικές τεχνικές και πειράματα ρόφησης-οξείδωσης μονοξειδίου του άνθρακα (CO stripping). Ερευνήθηκε η μείωση της περιεκτικότητας σε Pt χωρίς απώλειες της ηλεκτροκαταλυτικής ενεργότητας. Το TiO2 επιλέχθηκε λόγω της χημικής του σταθερότητας και του χαμηλού κόστους. Βρέθηκε ότι περιεκτικότητα σε TiO2 μέχρι 50% οδηγεί σε αύξηση της ηλεκτροχημικά ενεργής επιφάνειας (EAS) του ηλεκτροδίου.Η EAS του ηλεκτροδίου Pt(50%)-TiO2(50%) ήταν σχεδόν μια τάξη μεγέθους μεγαλύτερη από το ηλεκτρόδιο της καθαρής Pt, ενώ για περιεκτικότητα σε Pt χαμηλότερη από 30% η EAS μειώνεται δραματικά. Το παραπάνω συμπέρασμα στηρίχθηκε σε μετρήσεις του φορτίου της αναγωγικής κορυφής του οξειδίου της Pt και σε πειράματα ρόφησης-οξείδωσης του CO (CO stripping). Όλα τα δείγματα χρησιμοποιήθηκαν επίσης και ως άνοδοι κατά την διάρκεια ηλεκτροχημικής οξείδωσης μεθανόλης και αιθανόλης. Και στις δύο περιπτώσεις το ηλεκτρόδιο Pt(50%)-TiO2(50%) παρουσίασε τη μεγαλύτερη ηλεκτροκαταλυτική ενεργότητα. | el |
| dc.description.translatedabstract | In this study Pt-TiO2 binary electrodes were prepared by thermal decomposition of chloride precursors on Ti substrates, characterised by X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), X-ray Photoelectron Spectroscopy (XPS), electrochemical techniques and CO stripping and used as anodes for alcohol oxidation. The minimization of the Pt loading without electrocatalytic activity losses was also explored. TiO2 was chosen due to its chemical stability, low cost and excellent properties as substrate for Pt dispersion. It was found that TiO2 loading up to 50% results in Electrochemically Active Surface (EAS) increase. The EAS of Pt(50%)-TiO2(50%) was found to be almost one order of magnitude higher than that of pure Pt while for Pt loadings lower than 30% the EAS was diminished. The above conclusion has been confirmed both by following the charge of the reduction peak of platinum oxide and by CO stripping experiments. All samples have been evaluated during the electrochemical oxidation of methanol and ethanol. In both cases the Pt(50%)-TiO2(50%) electrode exhibited better electrocatalytic activity than the pure Pt anode. The observed higher performance of the binary electrodes has been attributed to the enhanced Pt dispersion as well as to the formation of smaller Pt particles by the addition of TiO2. | el |
| dc.identifier.uri | http://hdl.handle.net/10889/6354 | |
| dc.language.iso | gr | el |
| dc.relation.isformatof | Η ΒΚΠ διαθέτει αντίτυπο της διατριβής σε έντυπη μορφή στο βιβλιοστάσιο διδακτορικών διατριβών που βρίσκεται στο ισόγειο του κτιρίου της. | el |
| dc.rights | 0 | el |
| dc.subject | Διμεταλλικά ηλεκτρόδια | el |
| dc.subject | Κυψελίδες καυσίμου | el |
| dc.subject.alternative | Binary electrodes | el |
| dc.subject.alternative | Fuel cells | el |
| dc.subject.ddc | 621.312 42 | el |
| dc.title | Διμεταλλικά ανοδικά ηλεκτρόδια Pt-TiO2 για την ηλεκτροχημική οξείδωση αλκοολών σε κυψελίδες καυσίμου χαμηλών θερμοκρασιών | el |
| dc.title.alternative | Pt-TiO2 binary electrodes for alcohol oxidation in low temperature fuel cells | el |
| dc.type | Thesis | el |